Crystallographic texture of aluminum alloy samples produced by additive friction-stirred deposition

Abstract

The crystallographic texture formation in the AK9ch aluminum alloy (9.6% Si; 0.3% Mg; 0.1% Fe; 0.1% Mn, 15 Al balance) specimens manufactured using the Additive Friction Stir Deposition (AFS-D) technology at room16 temperature is investigated. The analysis was conducted using inverse pole figures (IPFs) obtained by X-ray17 diffraction methods. The results reveal the presence of shear, torsion, deformation, and recrystallization texture 18 components in both types of specimens. The texture of horizontal and vertical samples differs in the set of texture19 components and the character of their dispersion. The texture intensity of both types of specimens is ill-defined.This testifies to the possibility of manufacturing the AK9ch alloy components using AFS-D technology with 21 reduced anisotropy. Досліджено формування кристалографічної текстури у зразках алюмінієвого сплаву АК9ч (9,6% Si; 0,3% Mg; 0,1% Fe; 0,1% Mn, решта 15 Al), виготовлених за технологією адитивного тертя з перемішуванням (AFS-D) за кімнатної температури 16 . Аналіз проводився з використанням обернених полюсних фігур (IPF), отриманих методами рентгенівської дифракції 17 . Результати показують наявність компонентів текстури зсуву, кручення, деформації та перекристалізації в обох типах зразків. Текстура горизонтальних та вертикальних зразків відрізняється набором компонентів текстури 19 та характером їх дисперсії. Інтенсивність текстури обох типів зразків є нечітко визначеною. Це свідчить про можливість виготовлення компонентів зі сплаву АК9ч за технологією AFS-D 21 зі зниженою анізотропією.